It is a kind of hot stamping material which is made by coating and vacuum evaporation plus a layer of metal foil on the film base. Holographic metallic foil for paper & plastic.
It is a kind of hot stamping material which is made by coating and vacuum evaporation plus a layer of metal foil on the film base. Holographic metallic foil for paper & plastic.
1.Independent intellectual property formula, imported raw materials, can be adjusted according to customer requirements.
2.According to the standard volume cutting, also can adopt customer requirement to cut and wrap.
3.In the process of production, we use automatic adjusting temperature system and computer to control the coating to keep the goods peeling from film easily.
4.Maximum roll size: 150cm×12000m core: 3 inch
1.Independent intellectual property formula, imported raw materials, can be adjusted according to customer requirements.
2.According to the standard volume cutting, also can adopt customer requirement to cut and wrap.
3.In the process of production, we use automatic adjusting temperature system and computer to control the coating to keep the goods peeling from film easily.
4.Maximum roll size: 150cm×12000m core: 3 inch
Adhesive(Glue) Layer |
Aluminum Layer |
Hologram Layer |
Release Layer |
PET base film |
Adhesive(Glue) Layer |
Aluminum Layer |
Hologram Layer |
Release Layer |
PET base film |
Foil Name | Color | Thickness | Width | Length | Core Diameter |
LQ-101 | Gold | 12um | 64cm | 120m | 1 inch |
1、Thickness | 12um±0.2um | Test Method: DIN53370 |
2、Surface Tension | 29 --- 35Dyne/cm | |
3、Tension Strength(MD) | ≥220Mpa | Test Method: DIN53455 |
4、Tension Strength(TD) | ≥230Mpa | Test Method: DIN53455 |
5、Elongation at Break(MD) | ≤140% | Test Method: DIN53455 |
6、Elongation at Break(TD) | ≤140% | Test Method: DIN53455 |
7、Release Force | 2.5—5g | |
8、Shrinkage at 150℃/30min(MD) | ≤1.7% | Test Method: BMSTT11 |
9、Shrinkage at 150℃/30min(TD) | ≤0.5% | Test Method: BMSTT11 |
10、Thickness of Aluminum | 350±50X10(-10)M |
Foil Name | Color | Thickness | Width | Length | Core Diameter |
LQ-101 | Gold | 12um | 64cm | 120m | 1 inch |
1、Thickness | 12um±0.2um | Test Method: DIN53370 |
2、Surface Tension | 29 --- 35Dyne/cm | |
3、Tension Strength(MD) | ≥220Mpa | Test Method: DIN53455 |
4、Tension Strength(TD) | ≥230Mpa | Test Method: DIN53455 |
5、Elongation at Break(MD) | ≤140% | Test Method: DIN53455 |
6、Elongation at Break(TD) | ≤140% | Test Method: DIN53455 |
7、Release Force | 2.5—5g | |
8、Shrinkage at 150℃/30min(MD) | ≤1.7% | Test Method: BMSTT11 |
9、Shrinkage at 150℃/30min(TD) | ≤0.5% | Test Method: BMSTT11 |
10、Thickness of Aluminum | 350±50X10(-10)M |